The Effect of Ultrafast Heating on the Microstructure and Mechanical Properties of the 2.2 GPa Grade Hot Forming Steel

Abstract

The aim of the present work is to evaluate the effect of ultrafast heating on the microstructure and mechanical properties of hot forming steel. The initial microstructure utilized in this study was a cold-rolled microstructure, and the test steel was heated to full austenitization at a rate of 200 °C/s, followed by water quenching. It was observed that the ultrafast heating process significantly refines both the prior austenite grains and martensite laths while inheriting high-density dislocations from the initial cold-rolled microstructure. Consequently, the coupling mechanism between dislocation strengthening and grain refinement strengthening remarkably enhanced both the yield strength and ultimate tensile strength of the test steel. Eventually, the yield strength of the hot forming steel reached 1524 MPa, along with an ultimate tensile strength of 2221 MPa and uniform elongation of 5.2%.