Performance of a New Grouting Material under the Coupling Effects of Freeze–Thaw and Sulfate Erosion

Author:

Ma Qinyong12,Li Biao1

Affiliation:

1. School of Civil Engineering and Architecture, Anhui University of Science and Technology, Huainan 232001, China

2. Engineering Research Center of Underground Mine Construction, Ministry of Education, Anhui University of Science and Technology, Huainan 232001, China

Abstract

In order to study the performance of a new cement-based grouting material under the coupling of freeze–thaw cycle and sulfate erosion, tests related to the performance of the new grouting material were designed and carried out to analyze the damage mechanism of the material under the coupling of freezing and thawing and Na2SO4 solution by testing the mass change, relative dynamic elastic modulus, compressive strength loss and mineralogical and microstructural properties of the new grouting material. The test results show that with the increase in the number of freeze–thaw cycles, the mass loss and compressive strength loss of the specimens in 15% Na2SO4 solution gradually increased, and the relative dynamic elastic modulus showed a decreasing trend. When the freeze–thaw cycle number was 30, the mass loss rate, compressive strength loss rate and relative dynamic elastic modulus of the specimens in Na2SO4 solution were 4.17%, 24.59% and 84.3%, respectively, which showed better erosion and frost durability. Mineralogical and microstructural analysis showed that SO42− in solution led to the decomposition of the C-S-H gel and the formation of CaSO4•2H2O inside the specimen, and the internal deterioration was exacerbated by the widening of the crack width being aggravated, suggesting that the rate of material deterioration under the coupling of the two factors increased.

Funder

National Natural Science Foundation Project

Publisher

MDPI AG

Subject

General Materials Science

Reference24 articles.

1. Effect of sulfate attack on hydration of calcium aluminate cement at 5–40 °C;Wang;J. Chin. Ceram. Soc.,2019

2. Grouting diffusion mechanism in heterogeneous fault-fracture zone;Li;Adv. Eng. Sci.,2018

3. Zhu, X.F., Song, P.T., Du, F., Wang, J., Zhang, W., Zhou, Y.X., and Leng, F.G. (2021). Research on durability and water dispersibility of high performance shield grouting material. Concrete, 157–160.

4. Study on corrosion resistance of grouting materials for subsea tunnels and its engineering application;Jiao;Mod. Tunn. Technol.,2022

5. Effect of gypsum on properties of soda residue-fly ash slurry under compound activation;Liu;J. Yangtze River Sci. Res.,2019

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3