Affiliation:
1. College of Materials Science and Engineering, Sichuan University, Chengdu 610065, China
Abstract
Unsaturated titanium hydride (TiHX) powder has high formability and is a promising raw material for titanium-based powder metallurgy. In this work, TiH2, TiHX, and HDH Ti powders were characterized, the cold compaction behavior of the powders was investigated, and the densification mechanism was analyzed. The TiHX was a three-phase mixture containing an α plastic phase and δ and ε brittle phases through Rietveld refinement. The TiHX compacts had compressive strength of over 420 MPa (higher than TiH2 and similar to HDHTi) and relative density of over 80% (higher than TiH2 and HDH Ti) at 600 MPa. The Gerdemann–Jablonski and Cooper–Eaton equation were used to simulate the powder compaction curves and describe powder compaction behavior. The plastic deformation of TiHX powder is greater than TiH2, and the particle rearrangement is greater than HDH Ti during cold compaction. Such compaction behavior of TiHX causes an excellent green-strength–relative-density combination.
Funder
Technological breakthroughs in technological achievements of titanium powder metallurgy products
Subject
General Materials Science,Metals and Alloys
Reference30 articles.
1. Powder metallurgy of titanium—Past, present, and future;Fang;Int. Mater. Rev.,2018
2. Qian, M., and Froes, F.H. (2015). Titanium Powder Metallurgy: Science, Technology and Applications, Butterworth-Heinemann.
3. Strength–Ductility Property Maps of Powder Metallurgy (PM) Ti-6Al-4V Alloy: A Critical Review of Processing-Structure-Property Relationships;Kumar;Met. Mater. Trans. A,2017
4. Compaction of Titanium Powders;Gerdemann;Met. Mater. Trans. A,2010
5. The properties of powders. Part VI. The compressibility of powders;Walker;Trans. Faraday Soc.,1923
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献