Some Properties of Wood Plastic Composites Made from Rubberwood, Recycled Plastic and Silica

Abstract

The objective of this work was to evaluate some of the properties of experimental wood plastic composite (WPC) panels manufactured from a low percentage of rubberwood (Hevea brasiliensis Muell. Arg), waste polyethylene terephthalate (PET) and silica at three different ratios. It was determined that water absorption values of the samples decreased with the increasing amount of PET in the panels. The lowest absorption value of 0.34% was determined for the samples having 40% PET in their content as a result of 24-h soaking. The highest hardness value of 4492 N was found for the samples made with the combination of rubberwood, PET and silica at 10%, 40% and 50%, respectively. The compressive strength of WPC specimens also followed a similar trend with the hardness characteristics of the panel and improved with increasing PET percentage. Statistical analyses revealed that values of compression strength, hardness, 2-h and 24-h water absorption of the specimens made with 20, 30, and 40% PET content resulted in significant difference from each other (p ≤ 0.0001). Based on the findings in this study it appears that increasing silica content in the samples adversely influenced their mechanical properties while creating a certain level of enhancement of water absorption of the specimens. It seems that using a combination of waste PET and a limited amount of silica with a low percentage of wood particles could have the potential to produce value-added environmentally friendly composites to be used for different applications.