Synthesis and Characterization of Organo-Soluble Polyimides Based on Polycondensation Chemistry of Fluorene-Containing Dianhydride and Amide-Bridged Diamines with Good Optical Transparency and Glass Transition Temperatures over 400 °C

Abstract

Polymeric optical films with light colors, good optical transparency and high thermal resistance have gained increasing attention in advanced optoelectronic areas in recent years. However, it is somewhat inter-conflicting for achieving the good optical properties to the conventional thermal resistant polymers, such as the standard aromatic polyimide (PI) films, which are well known for the excellent combined properties and also the deep colors. In this work, a series of wholly aromatic PI films were prepared via the polycondensation chemistry of one fluorene-containing dianhydride, 9,9-bis(3,4-dicarboxyphenyl)fluorene dianhydride (FDAn) and several aromatic diamines with amide linkages in the main chain, including 9,9-bis [4-(4-aminobenzamide)phenyl]fluorene (FDAADA), 2,2′-bis(trifluoromethyl)-4,4′-bis[4-(4-aminobenzamide)] biphenyl (ABTFMB), and 2,2′-bis(trifluoromethyl)-4,4′-bis[4-(4-amino-3-methyl)benzamide] biphenyl (MABTFMB). The derived FLPI-1 (FDAn-FDAADA), FLPI-2 (FDAn-ABTFMB) and FLPI-3 (FDAn-MABTFMB) resins showed good solubility in the polar aprotic solvents, such as N-methyl-2-pyrrolidone (NMP), N,N-dimethylacetamide (DMAc) and dimethyl sulfoxide (DMSO). The solution-processing FDAn-PI films exhibited good optical transmittance over 80.0% at a wavelength of 500 nm (T500), yellow indices (b*) in the range of 1.01–5.20, and haze values lower than 1.0%. In addition, the FDAn-PI films showed low optical retardance with optical retardation (Rth) values in the range of 31.7–390.6 nm. At the same time, the FDAn-PI films exhibited extremely high glass transition temperatures (Tg) over 420 °C according to dynamic mechanical analysis (DMA) tests. The FDAn-PI films showed good dimensional stability at elevated temperatures with linear coefficients of thermal expansion (CTE) in the range of (31.8–45.8) × 10−6/K.