Chromophores’ Contribution to Color Changes of Thermally Modified Tropical Wood Species
Author:
Jurczyková Tereza1, Šárovec Ondřej1, Kačík František2ORCID, Hájková Kateřina1ORCID, Jurczyk Tomáš3, Hrčka Richard4ORCID
Affiliation:
1. Department of Wood Processing and Biomaterials, Faculty of Forestry and Wood Sciences, Czech University of Life Science Prague, Kamýcká 129, 165 21 Prague, Czech Republic 2. Department of Chemistry and Chemical Technology, Faculty of Wood Sciences and Technology, Technical University in Zvolen, T. G. Masaryka 24, 960 01 Zvolen, Slovakia 3. TIBCO Software s.r.o., Klimentská 1216/46, 110 00 Prague, Czech Republic 4. Department of Wood Science, Faculty of Wood Sciences and Technology, Technical University in Zvolen, T. G. Masaryka 24, 960 01 Zvolen, Slovakia
Abstract
This work examines the effect of thermal modification temperature (180, 200, and 220 °C) in comparison with reference (untreated) samples on selected optical properties of six tropical wood species—Sp. cedar (Cedrala odorata), iroko (Chlorophora excelsa), merbau (Intsia spp.), meranti (Shorea spp.), padouk (Pterocarpus soyauxii), and teak (Tectona grandis). The main goal is to expand the existing knowledge in the field of wood thermal modification by understanding the related degradation mechanisms associated with the formation of chromophoric structures and, above all, to focus on the change in the content of extractive substances. For solid wood, the CIELAB color space parameters (L*, a*, b*, and ΔE*), yellowness (Y), ISO brightness, and UV-Vis diffuse reflectance spectra were obtained. Subsequently, these wood samples were extracted into three individual solvents (acetone, ethanol, and ethanol-toluene). The yields of the extracted compounds, their absorption spectra, and again L*, a*, b*, ΔE*, and Yi parameters were determined. With increasing temperatures, the samples lose brightness and darken, while their total color difference grows (except merbau). The highest yield of extractives (mainly phenolic compounds, glycosides, and dyes) from thermally modified samples was usually obtained using ethanol. New types of extractives (e.g., 2-furaldehyde, lactones, formic acid, some monomer derivatives of phenols, etc.) are already created around a temperature of 180 °C and may undergo condensation reactions at higher temperatures. For padouk, merbau, teak, and partially iroko modified at temperatures of 200 and 220 °C, there was a detected similarity in the intensities of their UV-Vis DR spectra at the wavelength regions corresponding to phenolic aldehydes, unsaturated ketones, quinones, stilbenes, and other conjugated carbonyl structures. Overall, a statistical assessment using PCA sorted the samples into five clusters. Cluster 3 consists of almost all samples modified at 200 and 220 °C, and in the other four, the reference and thermally modified samples at 180 °C were distributed. The yellowness of wood (Y) has a very high dependence (r = 0.972) on its brightness (L*) and the yellowness index of the extractives in acetone Yi(Ac), whose relationship was described by the equation Y = −0.0951 × Y(Ac) + 23.3485.
Funder
Scientific Grant Agency of the Ministry of Education, Science, Research and Sport of the Slovak Republic and Slovak Academy of Sciences
Subject
Polymers and Plastics,General Chemistry
Reference85 articles.
1. Hon, D.N.S., and Shiraishi, N. (2001). Wood and Cellulosic Chemistry, Marcel Dekker. 2. The impact of natural and artificial weathering on the visual, color, and structural changes of seven tropical woods;Reinprecht;Eur. J. Wood Wood Prod.,2018 3. Panshin, A.J., and de Zeeuw, C. (1980). Textbook of Wood Technology, McGraw-Hill Book Company. 4. Chromophores in aged hardwood pulp—Their structure and degradation potential;Rosenau;Tappi J.,2008 5. Assessment of Chromophores in Chemically Treated and Aged Wood by UV-Vis Diffuse Reflectance Spectroscopy;Evtuguin;Cellul. Chem. Technol.,2016
|
|