Impact of Bark-Sourced Building Blocks as Substitutes for Fossil-Derived Polyols on the Structural, Thermal, and Mechanical Properties of Polyurethane Networks

Author:

Arshanitsa Alexandr1ORCID,Ponomarenko Jevgenija1,Pals Matiss1ORCID,Jashina Lilija1,Lauberts Maris1ORCID

Affiliation:

1. Latvian State Institute of Wood Chemistry, Dzerbenes Street 27, LV-1006 Riga, Latvia

Abstract

The hydrophilic extractives isolated from black alder (Alnus glutinosa) bark through hot water extraction were characterized as novel renewable macromonomers capable of forming polyurethane (PU) networks based on a commercial polyisocyanate, with partial or complete replacement of petroleum-derived polyol polyether. The bark-sourced bio-polyol mainly consists of the xyloside form of the diarylheptanoid oregonin, along with oligomeric flavonoids and carbohydrates, resulting in a total OH group content of 15.1 mmol·g−1 and a molecular weight (Mn) of approximately 750 g∙mol−1. The 31P NMR data confirmed a similar proportion of aliphatic OH and phenolic groups. Three-component PU compositions were prepared using polyethylene glycol (Mn = 400 g∙mol−1), bio-polyol (up to 50%), and polymeric diphenylmethane diisocyanate, which were pre-polymerized in tetrahydrofuran (THF) solution with tin organic and tertiary amine catalysts. The resulting mixture was cast and subjected to thermal post-curing. Calculation and experimental data confirmed the crosslinking activity of the bark-sourced bio-polyol in PU, leading to an increase in glass transition temperature (Tg), a decrease in sol fraction yield upon leaching of cured PU networks in THF, a significant increase in Young’s modulus and tensile strength. The macromonomers derived from bark promoted char formation under high temperature and oxidative stress conditions, limiting heat release during macromolecular network degradation compared to bio-polyol-free PU. It was observed that amine catalysts, which are active in urethane formation with phenolic groups, promoted the formation of PU with higher Tg and modulus at tensile but with less limitation of heat liberation during PU macromolecular structure degradation. The high functionality of the bark-derived bio-polyol, along with the equal proportion of phenolic and aliphatic OH groups, allows for further optimization of PU characteristics using three variables: increasing the substitution extent of commercial polyethers, decreasing the NCO/OH ratio, and selecting the type of catalyst used.

Funder

Latvian Council of Science

Publisher

MDPI AG

Subject

Polymers and Plastics,General Chemistry

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3