Li Zhong,Yang Peiyue,Zheng Zhongxiang,Pan Qiyun,Liu Yisi,Li Yao,Xuan Jinnan
Abstract
The effect of electrochemically active MnO2 as a coating material on the electrochemical properties of a Li1.2Mn0.54Ni0.13Co0.13O2 (LTMO) cathode material is explored in this article. The structural analysis indicated that the layered structure of the LTMO was unchanged after the modification with MnO2. The morphology inspection demonstrated that the rod-like LTMO particles were encapsulated by a compact coating layer. The MnO2 layer was able to hinder the electrolyte solution from corroding the LTMO particles and optimized the formation of a solid electrolyte interface (SEI). Meanwhile, lithium ions were reversibly inserted into and extracted from MnO2, which afforded an additional capacity. Compared with the bare LTMO, the MnO2-coated sample exhibited enhanced electrochemical performance. After the MnO2 coating, the first discharge capacity rose from 224.2 to 239.1 mAh/g, and the initial irreversible capacity loss declined from 78.2 to 46.0 mAh/g. Meanwhile, the cyclic retention climbed up to 88.2% after 100 cycles at 0.5 C, which was more competitive than that of the bare LTMO with a value of 71.1%. When discharging at a high current density of 2 C, the capacity increased from 100.5 to 136.9 mAh/g after the modification. These investigations may be conducive to the practical application of LTMO in prospective automotive Li-ion batteries.
Funder
National Natural Science Foundation of China
Natural Science Foundation of Hubei province of China
Subject
Electrical and Electronic Engineering,Mechanical Engineering,Control and Systems Engineering
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献