Author:
Wang Zhaojie,Zhang Guowei,Kang Yuanyuan,Liu Yijun,Ren Xiaoyan
Abstract
We studied the effects of adding Y on the microstructure, mechanical properties and wear properties of ZCuSn10Pb10, and clarified the underlying mechanism by microstructure characterization through SEM, EDS and XRD. No new phase was detected after the addition of Y up to 0.2 wt.%, but an enrichment of Y in the Pb phase was found. The Pb particles were refined significantly after the addition of Y, which resulted from the compositional undercooling for the Cu dendrite where the Pb particles solidified, and the highest refinement efficiency was reached when the content of Y was 0.15 wt.%. The hardness of the alloy was improved due to the refinement of the microstructure. The fine Pb particles between the dendrite branches acted as solid lubricant, which was smeared on the entire surface during a friction and wear experiment, thus increasing wear resistance and reducing the coefficient of friction.
Funder
the Opening Project of Shanxi Key Laboratory of Controlled Metal Solidification and Precision Manufacturing, North University of China
Subject
General Materials Science
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献