Investigations of the Influence of Nano-Admixtures on Early Hydration and Selected Properties of Calcium Aluminate Cement Paste

Author:

Boris Renata,Wilińska IwonaORCID,Pacewska Barbara,Antonovič Valentin

Abstract

In this work, the hydration of calcium aluminate cement (CAC, Al2O3 ≥ 70%) paste with nano admixtures (0, 0.05%, 0.1% and 0.2%) of nano-silica (NS) and carbon nano-cones (NC) when W/CAC = 0.35 was investigated. The methods of calorimetry, thermal analysis, X-ray diffraction (XRD), IR spectroscopy, and scanning electron microscopy (SEM) were used. In addition, the physical and mechanical properties of hardened cement pastes were determined after 3 days of hardening. NS was found to shorten the induction period of CAC hydration and accelerate the time of the secondary heat release effect, especially in the specimens with the highest NS content. The incorporation of NC (up to 0.2%) slows down the hydration process. After 3 days of hydration, the formation of hydration products, such as C2AH8, CAH10, C3AH6 and AH3 hydrates, was observed in CAC pastes, however, the quantitative compositions were different depending on the kind of nano admixture and its amount. SEM results obtained show differences in the effect of NS and NC on the formation of the structure of cement paste during its hardening. Significant changes in CAC paste microstructure were caused by the addition of NS and NC admixtures. Compressive strength was found to increase with the increase of NS and the optimal NS content was found to be 0.10 wt.%. The modification of the cement paste with an NS admixture results in a higher amount of hydrates, lower total porosity, and a higher amount of the smallest pores in the microstructure of the sample. NS and NC influence the hydration behaviour of CAC in different ways, which causes characteristic changes in the microstructure and properties of hardened samples.

Funder

European Social Fund under grant agreement with the Research Council of Lithuania (LMTLT).

Publisher

MDPI AG

Subject

General Materials Science

Reference50 articles.

1. Influence of curing temperature on the physicomechanical, characteristics of calcium aluminate cement with air-cooled slag or water-cooled slag;Heikal;Ceram. Sil.,2004

2. Nanotechnology in castable refractory

3. How cool are refractory materials?;Garbers-Craig;J. S. Afr. Inst. Min. Metall.,2008

4. A study on mechanical and physical properties of monocalcium aluminate cement reinforced with nano-SiO2 particles

5. A study on mechanical and pressure-sensitive properties of cement mortar with nanophase materials

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3