Zhang Shuo,Song Jiangfeng,Liao Hongxin,Liu Yanglu,Zhang Gen,Ma Shida,Tang Aitao,Atrens Andrej,Pan Fusheng
Abstract
The effect of B addition on the microstructure and mechanical properties of AM50 was investigated, and the mechanism of grain refinement was clarified. Optical microscopy, X-ray diffraction, scanning electron microscopy, and electron probe microanalysis were used to characterize the microstructure evolution. The grain size of as-cast AM50 decreased from 550 μm to 100 μm with the B content increasing from 0 to 0.15 wt.%. AlB2 particles in the Al-3B master alloy transformed to Mg-B, and acted as the grain refiner. The addition of B to as cast AM50 alloy results in improved mechanical properties of AM50 + xB alloys. For instance, the YTS (yield tensile strength), UTS (ultimate tensile strength), and elongation of as cast AM50 + 0.15 wt.% B alloy was 94 MPa, 215 MPa, and 12.3%.
Funder
National Natural Science Foundation of China
Key Technologies Research and Development Program
Subject
General Materials Science
Cited by
8 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献