A Sodium Bis(fluorosulfonyl)imide (NaFSI)‐based Multifunctional Electrolyte Stabilizes the Performance of NaNi1/3Fe1/3Mn1/3O2/hard Carbon Sodium‐ion Batteries

Abstract

AbstractA sodium bis(fluorosulfonyl)imide (NaFSI)‐based multifunctional electrolyte is developed by partially replacing NaPF6 salt in the electrolyte to improve the wide temperature range working capability of NaNi1/3Fe1/3Mn1/3O2/hard carbon (NNFM111/HC) sodium‐ion batteries (SIBs). The capacity retention of the SIBs with NaFSI‐NaPF6 dual salt electrolyte increases from 47.2 % to 75.5 % after 250 cycles at 25 °C, and from 51.0 % to 82.3 % after 80 cycles at 45 °C, and the 1 C discharge capacity retention at the low temperature of −20 °C also increases 26.8 %. In the single salt system, NaPF6 effectively passivate the aluminum foil and NaFSI passivate the electrode/electrolyte interface. The synergistic effect of NaPF6 and NaFSI greatly improves the battery performance in a wide temperature range. This NaFSI‐based dual salt electrolyte also effectively overcomes the flaws when the SIBs using NaFSI or NaPF6 independently, and makes it more suitable for SIBs, indicating promising prospects in the commercial application of NNFM111/HC SIBs.