Microstructure, Mechanical, and Corrosion Performance of AA4343/AA3003/AA4343 Laminated Sheets Subjected to Cryorolling and Annealing

Author:

Samdane Golam1,Guo Baohong1,Cui Huijie2,Kong Charlie3,Yu Hailiang1ORCID

Affiliation:

1. State Key Laboratory of Precision Manufacturing for Extreme Service Performance Light Alloy Research Institute Central South University Changsha 410083 China

2. Shimadzu (China) Co., Ltd. Shanghai 200233 China

3. Mark Wainwright Analytical Centre University of New South Wales Sydney NSW 2052 Australia

Abstract

The effects of cryorolling (CR), hot rolling (HR), and different annealing temperatures on the microstructure, mechanical, and corrosion performance of AA4343/AA3003/AA4343 laminated sheets are studied. Compared with the HR samples, the microstructure of the CR samples presents a significant decrease in the size of elongated grains and significantly large second‐phase particles Al(Mn, Fe)Si in the AA3003 alloy. Grains in CR samples subjected annealing at 200–300 °C become finer. Increasing to 400–550 °C, the grains begin to grow, and the Si is diffused into the core layer. A comparison of HR and CR processing reveals a significant increase in the yield strength from 153 to 209 MPa and the ultimate tensile strength from 168 MPa to 217 MPa of the laminated sheet. Potentiodynamic polarization measurements and immersion tests are conducted to assess the corrosion morphology. After being immersed in a 3.5% NaCl solution for two weeks, the clad surface of the laminated sheet exhibits uniform corrosion products and pitting corrosion, which shows the pitting corrosion depth of the CR sample improved compared to the HR sample. The study suggests that both CR and annealing can be useful for enhancing the mechanical properties, and corrosion morphology of laminated sheets.

Publisher

Wiley

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3