Abstract
AbstractPolyurethane has been extensively studied as a multifunctional material for water‐lubricated bearing materials. As one of the polyurethane elastomeric synthetic material, the content of 4,4′‐methylene bis(2‐chloroaniline) (MOCA) directly affects the intermolecular structure and thus the properties of the material. Five samples with different MOCA contents were prepared by casting molding and tested. The results showed that the optimal comprehensive performance was obtained when the ratio of the amino group to the hydrocyanic acid group was 0.95, with tensile, compressive, and bending strengths of 50.1, 91.8, and 12.6 MPa, respectively. Compared with other samples, the surface of the sample was smooth, which was conducive to the formation of the water film. The bearing capacity and lubrication condition are improved, and the best tribological performance was shown. This research for the application of polyurethane elastomer on the water‐lubricated bearing provides a theoretical basis.
Funder
Innovative Research Group Project of the National Natural Science Foundation of China
Subject
Materials Chemistry,Polymers and Plastics,Surfaces, Coatings and Films,General Chemistry
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献