Development of highly conductive hybrid Ni‐biocarbon‐based polyvinyl alcohol composites for microwave shielding properties

Abstract

AbstractIn this study a highly flexible microwave shielding material was fabricated by solution casting method utilizing Nickel and biocarbon particles in PVA matrix and characterized for mechanical, magnetic, and microwave shielding properties. The main aim of this study was to prove the significant role of magnetic particles in electromagnetic interference (EMI) shielding along with conductive particles. The results show that the addition of Ni‐biocarbon hybrid particle increases the shielding properties up to 56.5 dB at 20 GHz. The magnetic permeability increased gradually with the inclusion of Ni particles with a highest magnetization, coercivity, and retentivity of 1250 E−6 emu, −9000 G, and 1100 E−6 emu. Similarly the mechanical results show that adding biocarbon enhances the composite's mechanical properties. A highest tensile strength, tear strength, elongation, and hardness are noted as 38, 168 MPa, 18.4%, and 36 Shore‐D. Comparatively, the hardness and elongation% of composite designations contains 3 and 5 vol% of hybrid particles have increased by 9% and 26%, respectively, in comparison to composite containing only 5 vol% of biocarbon with PVA. Scanning electron microscope fractography indicates biocarbon particles reduce voids and improve adhesion. These flexible EMI shielding composites could be used in telecommunication and other wave transmitting devices in engineering applications.