DeoxyriboNucleic acid‐enhanced carbon nanotube dispersed epoxy resin composites: Mechanical and thermal properties study

Abstract

AbstractThe homogeneous dispersion of multi‐walled carbon nanotubes (MWCNTs) in a polymer matrix significantly affects the overall properties of composites. In this study, MWCNTs/epoxy (EP) composites were prepared using DeoxyriboNucleic acid (DNA) as a dispersant. The MWCNTs were uniformly dispersed in a phenalkamine curing agent and crosslinked with an epoxy resin matrix. The non‐covalent functionalization of DNA‐dispersed MWCNTs was confirmed by characterizing both the pristine and DNA‐modified MWCNTs. Additionally, the dispersion state and stability of MWCNTs in the curing agent solution were evaluated. Tensile strength and single‐lap‐shear (SLS) were employed to assess the mechanical properties of the composites. The results indicated that the DNA‐dispersed MWCNTs composites exhibited superior strength and toughness, with tensile and shear strengths of 46.81 and 19.64 MPa, respectively, at optimal ratios. These values represent increases of 68.38% and 50.96% compared to pure EP. Dynamic mechanical thermal analysis (DMTA) revealed that the energy storage modulus of DNA‐dispersed MWCNTs/EP composites increased to 2722 MPa, a 24.7% enhancement over pure EP. Furthermore, the thermal properties of the composites were thoroughly investigated. Thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) showed that the initial decomposition temperature of the DNA‐assisted dispersed composites rose to 330°C. The macromolecular relaxation of the EP materials occurred at higher temperatures, leading to an increased glass transition temperature.Highlights DNA was used to disperse MWCNTs in phenalkamine curing agent. MWCNTs/EP composites were made by crosslinking DNA‐dispersed MWCNTs with epoxy resin. DNA‐dispersed MWCNTs boosted tensile and lap shear strength. Thermal properties improved due to DNA‐dispersed MWCNTs, and increased the energy storage modulus of the composite.