Abstract
AbstractIn this article, sulfonated calixarene was used to modify Mg‐Al hydrotalcite (Mg‐Al‐LDH) prepared by coprecipitation method to improve the interfacial compatibility between nano‐hydrotalcite and waterborne polyurethane (WPU) matrix. Waterborne polyurethane hydrotalcite nanocomposite emulsion (STCR‐LDH/WPU) was prepared by adding modified hydrotalcite into WPU. The tensile strength, surface static contact angle, water permeability rate, and water absorption of the film were measured. FTIR and X‐ray diffraction were used to determine the film‐forming properties. The results showed that the tensile strength increased to 57 MPa, the elongation at break reached 292%, and its water vapor permeability and UV resistance were significantly improved by introducing sulfonated calixarene to modify the hydrotalcite nanosheet structure based on WPU. The compound emulsion gives the coated leather excellent physical and mechanical properties, and the laminated leather has stronger coating abrasion resistance.
Funder
National Natural Science Foundation of China
Reference28 articles.
1. Synthetic talc as catalyst and filler for waterborne polyurethane-based nanocomposite synthesis
2. Water‐based polyurethane leather finishing agent production, application and development;Wu GB;Technol Dev Enterprise,1997
3. Application of aqueous polyurethane in finishing of synthetic leather;Shi HH;China Leather,2008
4. Research progress of room temperature crosslinking system for acrylic leather finishing;Qiang XH;Fine Chem,2011
5. Research progress in preparation and flame retardancy of polymer/LDH nanocomposites;Lv B;Fine Chem,2019
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献