Effects of Moulding Sand Permeability and Pouring Temperatures on Properties of Cast 6061 Aluminium Alloy

Abstract

Effects of moulding sand permeabilities prepared from the combinations of four proportions of coarse and fine particle size mixtures and pouring temperatures varied from 700, 750, and 800 (±10°C) were studied on the hardness, porosity, strength, and microstructure of cast aluminium pistons used in hydraulic brake master cylinder. Three sand moulds were prepared from each of the 80 : 20, 60 : 40, 40 : 60, and 20 : 80 ratios. The surfaces and microstructures of cast samples were examined using high resolution microscopic camera, metallurgical microscope with digital camera, and scanning electron microscope with EDX facilities. The best of the metallurgical properties were obtained from the combination of 80 : 20 coarse-fine sand ratio and 750 ± 10°C pouring temperature using as MgFeSi inoculant. An 8 : 25 ratio of coarse to fine grained eutectic aluminium alloy was obtained with enhanced metallographic properties. The cast alloy poured at 750 ± 1°C has a large number of fine grain formations assuming broom-resembling structures as shown in the 100 µm size SEM image.