The effect of annealing temperature on electrical characteristics of iridium (Ir) and iridium/gold (Ir/Au) Schottky contacts to n-type InGaN have been investigated by means of current-voltage (I-V) and capacitance-voltage (C-V) techniques. It is observed that the barrier height of Ir/n-InGaN and Au/Ir/n-InGaN Schottky diodes increases after annealing at 300∘C for 1 min in N2 ambient compared to the as-deposited. However, the barrier heights are found to be decreased somewhat after annealing at 500∘C for the both Ir and Ir/Au Schottky contacts. From the above observations, it is clear that the optimum annealing temperature for both Ir and Ir/Au Schottky contacts is 300∘C. Moreover, the barrier height (ϕb), ideality factor (n) and series resistance (RS) are determined using Cheung’s and Norde methods. Besides, the energy distribution of interface state densities are determined from the forward bias I-V characteristics by taking into account the bias dependence of the effective barrier height. Based on the above results, it is clear that both Ir and Ir/Au Schottky contacts exhibit a kind of thermal stability during annealing.
Funder
University Grants Commission
Cited by
10 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献