Effect of MWCNT on Thermal, Mechanical, and Morphological Properties of Polybutylene Terephthalate/Polycarbonate Blends

Abstract

This paper evaluated the effect of multiwall carbon nanotube (MWCNT) on the properties of PBT/PC blends. The nanocomposites were obtained by melt blending MWCNT in the weight percentages 0.15, 0.3, and 0.45 wt% with PBT/PC blends in a high performance corotating twin screw extruder. Samples were characterized by tensile testing, dynamic mechanical analysis, thermal analysis, scanning electron microscopy, and X-ray diffraction. Concentrations of PBT and PC are optimized as 80 : 20 based on mechanical properties. A small amount of MWCNT shows better increase in the thermal and mechanical properties of the blends of PBT/PC nanocomposite when compared to nanoclays or inorganic fillers. The ultimate tensile strength of the nanocomposites increased from 54 MPa to 85 MPa with addition of MWCNT up to 0.3% and then decreased.The tensile modulus values were increased to about 60% and the flexural modulus was more than about 80%. The impact strength was also improved with 20% PC to about 60% and with 0.15% MWCNT to about 50%. The HDT also improved from 127°C to 205°C. It can be seen from XRD result that the crystallinity of PBT is less affected by incorporating MWCNT. The crystallizing temperature was increased and the MWCNT may act as a strong nucleating agent.