PMMA thin films were deposited by sol gel spin coating method on ITO substrates. Toluene was used as the solvent to dissolve the PMMA powder. The PMMA concentration was varied from 30 ~ 120 mg. The dielectric properties were measured at frequency of 0 ~ 100 kHz. The dielectric permittivity was in the range of 7.3 to 7.5 which decreased as the PMMA concentration increased. The dielectric loss is in the range of 0.01 ~ –0.01. All samples show dielectric characteristics which have dielectric loss is less than 0.05. The optical properties for thin films were measured at room temperature across 200 ~ 1000 nm wavelength region. All samples are highly transparent. The energy band gaps are in the range of 3.6 eV to 3.9 eV when the PMMA concentration increased. The morphologies of the samples show that all samples are uniform and the surface roughness increased as the concentration increased. From this study, it is known that, the dielectric, optical, and morphology properties were influenced by the amount of PMMA concentration in the solution.
Funder
Research Management Institute
Subject
General Engineering,General Materials Science
Cited by
32 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献