Composites Based Green Poly(L-Lactic Acid) and Dioctyl Phthalate: Preparation and Performance

Abstract

The effects of dioctyl phthalate (DOP) on performances of poly(L-lactic acid) (PLLA) were investigated in detail using optical depolarizer, X-ray diffraction, melt index instrument, and electronic tensile tester. Crystallization performance showed that the half time of overall PLLA crystallizationt1/2decreased with increasing of crystallization temperature (80°C to 105°C), but thet1/2of PLLA/DOP composites firstly decreased and then increased, andt1/2of PLLA/DOP exhibited minimum value at 85°C. Compared to neat PLLA, 20%DOP made thet1/2decrease from 7258.3 s to 265.4 s. X-ray diffraction experiment further confirmed that DOP could accelerate the crystallization of PLLA. The fluidity of PLLA/DOP composites indicated that the melt mass flow rate firstly decreased and then greatly increased with increasing of DOP content. The mechanical performance showed that DOP could improve the general mechanical performance, and the elongation at break of PLLA/25%DOP was about 30 times longer than that of neat PLLA.