The Effect of Ultraviolet Wavelength on Corrosion Behavior of 7075 Aluminum Alloy in the Marine Atmospheric Environment

Abstract

The influence of ultraviolet rays on the corrosion behavior of 7075 aluminum alloy in the marine atmosphere was studied by salt spray corrosion test. Electrochemical methods and surface analysis techniques were used to analyze and compare the corrosion laws of 7075 aluminum alloy in the marine atmosphere under ultraviolet radiation with wavelengths of 0 nm, 185 nm, 254 nm, and 365 nm. The results showed that ultraviolet light irradiation could promote the corrosion of 7075 aluminum alloy. Oxygen was prone to chemical reactions to form oxygen atoms after being irradiated by ultraviolet rays, and oxygen atoms recombined with oxygen to form ozone in the marine atmosphere. The 7075 aluminum alloy in the marine atmosphere accelerated corrosion due to the increasing ozone content. Although there were passivation films with different degrees of protection on the surface of aluminum alloy under ultraviolet irradiation, the surface of 7075 aluminum alloy in the marine atmosphere failed to form a stable passivation film after pitting, and the corrosion rate was the fastest when the ultraviolet wavelength was 185 nm.