Affiliation:
1. Department of Materials Science, Faculty of Science, Chulalongkorn University, Bangkok 10330, Thailand
2. Center of Excellence on Petrochemical and Materials Technology, Chulalongkorn University, Bangkok 10330, Thailand
Abstract
Soybean oil modified cellulose fibril (Oil-g-CF) and organosilane modified cellulose fibril (Silane-g-CF) were prepared using maleinized soybean oil and hexadecyltrimethoxysilane, respectively. Thus obtained modified cellulose fibril was added to polypropylene by a simple melt mixing on a hotplate. PP/modified CF composites with 4.0 wt% filler content were prepared. The composites were subject to a polarized optical microscope to investigate particle dispersion, supramolecular morphology, and crystallization behavior. It was found that Silane-g-CF exhibited smaller particle sizes with better particle distribution when compared to Oil-g-CF. In addition, the etched composite samples unveiled an increase in a number of spherulite crystals as well as a decrease in the spherulite size. The nonisothermal crystallization study of composites revealed that both Oil-g-CF and Silane-g-CF were capable of nucleating PP by facilitating faster crystallization process and raising the number of spherulites. The DSC results indicated that Silane-g-CF was able to perform a more effective nucleation than Oil-g-CF, judged by a higher crystallization temperature. Moreover, PP composites containing Oil-g-CF and Silane-g-CF had higher crystallinity by 7% and 10%, for the first and the latter, respectively, when compared to neat PP.
Subject
General Engineering,General Materials Science
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献