The CFRTP and the stainless steel were joined by the fiber laser, and the effect of processing parameters on the joint quality was investigated in detail. The heat-affected zone on the stainless steel and the microstructure of the joint interface were examined and analyzed. The results showed that the laser joining process refines the microstructure of the fusion and heat-affected zones in the stainless steel. And the tensile strength of the joint was affected greatly by the laser power and scanning speed but slightly by the clamping pressure. With the PPS additive, the joint shear strength could be improved, and the optimal PPS additive thickness is 300 μm. With the best parameters, joint with a shear strength of 15–17 MPa could be obtained as the laser power is 320–350 W, the scanning speed is 4-5 mm/s, the clamping pressure is about 0.5 Mpa, and the additive PPS thickness is about 300 μm.
Funder
Shenzhen Basic Research Project
Subject
General Engineering,General Materials Science
Cited by
28 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献