Surface Microstructure of Two Bioceramics: Calcium-Enriched Mixture and Cold Ceramic in Setting Environments with Different pH Values

Abstract

Introduction. The pH of the setting environment could alter the surface characteristics of bioceramics. The present study aimed to assess the surface microstructure of calcium-enriched mixture (CEM cement) and cold ceramic (CC) in setting environments with different pH values. Materials and Methods. 12 dentin blocks with 3 mm height and internal diameter were prepared. CEM cement and CC were prepared and packed into the blocks. Samples in each bioceramics group (n = 6) were divided into 3 subgroups (n = 2) and exposed to acid, pH of 7.4, and alkaline pH for 1 week. Specimens were prepared for evaluation under a scanning electron microscope using backscattered electron (BSE) detectors. Monitoring of pH changes was rendered with a pH meter through the setting process. Results. BSE detection in an acidic environment showed more amorphous microstructures in CC specimens in comparison to CEM cement. In pH of 7.4 and alkaline pH, more unhydrated structures were observed in CEM cement compared with CC samples. During the first 48 h of the setting process, the pH changes of setting environments were more rapid in the CEM cement group in comparison to CC samples. Conclusion. pH changes during the setting process of cement could affect the surface microstructure and physical properties. In acidic environments, the crystallization of CC cement is more disrupted than that of CEM cement.