Localised coating failure of epoxy coated aluminium alloy 2024–T3 in 0.5M NaCl solutions: comparison of conventional electrochemical techniques and microelectrochemical methods-Reference-Cited by-同舟云学术

Localised coating failure of epoxy coated aluminium alloy 2024–T3 in 0.5M NaCl solutions: comparison of conventional electrochemical techniques and microelectrochemical methods

Published:2003-06 Issue:2 Volume:38 Page:119-128
ISSN:1478-422X
Container-title:Corrosion Engineering, Science and Technology
language:en
Short-container-title:Corrosion Engineering, Science and Technology

Author:

Schneider O.,Kelly R. G.

Publisher

Informa UK Limited

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Link

http://www.tandfonline.com/doi/pdf/10.1179/147842203767789195

Reference63 articles.

1. Inhibition of Pitting Corrosion on Aluminum Alloy 2024-T3: Effect of Soluble Chromate Additions vs Chromate Conversion Coating

2. Copper Redistribution during Corrosion of Aluminum Alloys

3. Local Dissolution Phenomena Associated with S Phase ( Al2CuMg ) Particles in Aluminum Alloy 2024‐T3

4. Evidence for Cu Ion Formation by Dissolution and Dealloying the Al[sub 2]CuMg Intermetallic Compound in Rotating Ring-Disk Collection Experiments

5. T. SUTER and R. C. ALMLIE: in 'Critical factors in localised corrosion III', (ed. R. G. Kelly et al), PV 98–17, 118–129; 1999, Pennington, NJ, Electrochemical Society.

Cited by 14 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Key parameters and mechanism of blistering of coil-coatings in humid-hot laboratory environments;Progress in Organic Coatings;2023-02

2. The Influence of the Nature of Anions on the Adhesion Durability of Bitumen–Anionite Protective Systems;Protection of Metals and Physical Chemistry of Surfaces;2022-06

3. Investigation of Polypyrrole Coatings Containing Nanosized Metal Oxides for Corrosion Protection of AA2024 Al Alloy;J ELECTROCHEM SCI TE;2019

4. A comparative study on corrosion kinetic parameter estimation methods for the early stage corrosion of Q345B steel in 3.5wt% NaCl solution;International Journal of Minerals, Metallurgy, and Materials;2017-10

5. Differential scanning calorimetry and optical photo microscopy examination for the analysis of failure of fusion bonded powder epoxy internal coating;Engineering Failure Analysis;2015-10