Heap sulphuric-thiocyanate leaching of gold and uranium

Published:2024-01-10 Issue:4 Volume:27 Page:821-828
ISSN:2782-6341
Container-title:iPolytech Journal
language:
Short-container-title:jour

Author:

Shipnigov A. A.¹,Epiforov A. V.¹,Sobennikov R. M.¹,Musin E. D.¹,Balikov S. V.¹

Affiliation:

1. Irkutsk Research Institute of Precious and Rare Metals and Diamonds

Abstract

The article evaluates the main parameters of simultaneous heap leaching of gold and uranium from oxidised gold-uranium ore using sulphuric acid thiocyanate solutions. Pilot tests for the simultaneous heap leaching of gold and uranium were carried out using oxidised crushed gold-uranium ore with a size of -40+0 mm. The gold and uranium content in the ore was 0.80 and 266 g/t, respectively. Experiments were carried out using a percolation column with a diameter of 300 mm and a height of 2000 mm The ore mass in the column was 180 kg. The temperature during the tests was in the range of 17–25°C. Leaching was carried out under the following conditions: H2SO4 concentration – 5 g/dm3, SCN– concentration – 0.5 g/dm3, Eh – 490–510 mV, Fe3+ ion concentration – 1.0–1.5 g/dm3. Acid-soluble minerals contained in the ore comprised the source of iron ions. Hydrogen peroxide was used to oxidise Fe2+ ions. Pilot tests were carried out in a closed cycle with separate sorption of gold and uranium. Based on the research results, gold recovery reached 90%, while uranium recovery was 55%. Following gold and uranium leaching, the loaded activated carbons and ion exchange resins were obtained. It was established that the gold content on activated carbons was 0.5–0.6 mg/g, while the uranium content on ion exchange resins amounted to 30–35 mg/g. The reagent consumption was as follows: H2SO4 – 10.5 kg/t, KSCN – 0.94 kg/t, H2O2 – 0.65 kg/t. It is shown that the technology for simultaneous heap leaching of gold and uranium with sulphuric acid thiocyanate solutions offers efficient processing of the ore. The recovery rates of gold and uranium are comparable to those obtained during pilot tests for heap leaching of the ore using conventional technology, involving the individual twostage leaching of these metals using sulphuric acid and cyanide solutions.

Publisher

Irkutsk National Research Technical University

Reference22 articles.

1. Kotlyar Yu. A., Meretukov M.A., Strizhko L.S. Metallurgy of precious metals. Moscow: Ore and Metals; 2005, 432 p. (In Russ.).

2. Shipnigov A.A., Sobennikov R.M., Epiforov A.V., Musin E.D. Heap leaching of oxidized gold-uranium ores. In: Nauchnye osnovy i praktika pererabotki rud i tekhnogennogo syr'ya: materialy XXVII Mezhdunarodnoj nauchno-tekhnicheskoj konferencii = Scientific foundations and processing practice of ores and technogenic raw materials: materials of the 27th International scientific and technical conference. 7–8 April, 2022, Yekaterinburg, Yekaterinburg: Ural State Mining University; 2022, p. 190-194. (In Russ.).

3. Shipnigov A.A., Sobennikov R.M., Epiforov A.V., Musin E.D., Grigoriev S.G. Heap leaching of gold and uranium from oxidized gold-uranium ore. Ratsionalnoe osvoenie nedr. 2022;2:66-71. (In Russ.). https://doi.org/10.26121/RON.2022.73.14.009. EDN: BDRHMA.

4. Robinson R.E. Status report from South Africa. In: Processing of low-grade uranium ores. 27 June – 1 July 1966, Vienna. Vienna: International Atomic Energy Agency; 1967, р. 33-37.

5. Fleming C.A. A process for simultaneous recovery of gold and uranium from South African ores. In: Gold 100-Proceeding of the International Conference on Gold. Extractive Metallurgy of Gold, South African Institution of Mining and Metallurgy. Johannesburg; 1986, vol. 2, р. 301-309.