Author:
Koltsova Y.I., ,Ovcharenko V.I.,
Abstract
This study was aimed at producing a porous layered glass ceramic material with a decorative-protective coating via one-stage firing. Waste products were used as gas-forming agents to fabricate a glass ceramic material, which partially solves a problem of their utilization; available natural raw materials were also used as gas-forming agents. A decorative-protective coating was applied simultaneously with the formation of the main layers of the material. It consisted of glass cullet and various amounts of coloring oxide. Firing of the samples was carried out at the temperature of 7500С. The coating containing 99.9 wt.% of glass cullet and 0.1 wt.% of Cr2O3 with the thickness of 425 m and having a greenish color was stated to be the coating of the highest quality. As a result of the research, a three-layer porous glass ceramic material was obtained with a low coefficient of thermal conductivity (0.056 W m–1 K–1). The presence of a fourth front decorative-protective layer will allow using this material in construction as a heat-insulating and structural material without additional cladding.
Publisher
SHEI Ukrainian State University of Chemical Technology
Subject
Materials Chemistry,General Chemical Engineering,Environmental Chemistry,General Chemistry
Reference16 articles.
1. 1. Fernandes HR, Tulyaganov DU, Ferreira JMF. Preparation and characterization of foams from sheet glass and fly ash using carbonates as foaming agents. Ceram Int. 2009; 35(1): 229-235. doi: 10.1016/j.ceramint.2007.10.019.
2. 2. Wang X, Feng D, Zhang B, Li Z, Li C, Zhu Y. Effects of KNO3 on the microstructure and physical properties of glass foam from solid waste glass and SiC powder. Mater Lett. 2016; 169: 21-23. doi: 10.1016/j.matlet.2015.12.076.
3. 3. Souza MT, Maia BGO, Teixeira LB, de Oliveira KG, Teixeira AHB, de Oliveira APN. Glass foams produced from glass bottles and eggshell wastes. Process Saf Environ Prot. 2017; 111: 60-64. doi: 10.1016/j.psep.2017.06.011.
4. 4. Guo Y, Zhang Y, Huang H, Meng K, Hu K, Hu P, et al. Novel glass ceramic foams materials based on red mud. Ceram Int. 2014; 40(5): 6677-6683. doi: 10.1016/j.ceramint.2013.11.128.
5. 5. Kaz'mina OV, Vereshchagin VI, Abiyaka AN. Rasshireniye syr'yevoi bazy dlya proizvodstva penosteklokristallicheskikh materialov [Expansion of raw materials base for production of foam glass ceramics]. Stroitel'nye Materialy. 2009; (7): 54-55. (in Russian).