Protective and decorative properties of titanium glass enamels

Abstract

It is known that enamel coatings with enhanced protective and decorative properties can be fabricated on the basis of boron-silicate glass frits with an increased content of TiO2 in their composition. Opacity and white color of enamel coatings are due to their crystallization at firing temperatures. Titanium glass enamels are not pure white visually, and show yellow and blue shades depending on their chemical composition. The purpose of this work was to establish the influence of basic components on the water resistance and color characteristics of titanium enamel coatings. Our experimental study was focused on the glass frits with the chemical composition described by the generalized formula (76–n–m)SiO2nB2O3mNa2O24MexOy, where MexOy is the total content of TiO2, ZrO2, Al2O3, MgO, СaO, P2O5, and K2O. It was found that the glass frits with the following content of basic components (mol.%): Na2O 12–13, K2O 3, B2O3 10–11, SiO2 49–51 demonstrated the highest water-resistant properties. The color characteristics of titanium enamel coatings prepared on the basis of the mentioned glass frits differ significantly from the reference white light A; the titanium enamel coatings under consideration have a yellow-green tint. The highest deviations of the enamel coating color purity and color tone from a standard of white color were observed when increasing the Na2O content in the glass frits composition at the expense of SiO2. The color of titanium coatings with the highest water resistance has a deviation from the standard of white color within 4–6%.