LI Xianfeng,XIA Cunjuan,WU Yi,CHEN Dong,WANG Mingliang,MA Naiheng,WANG Haowei
Abstract
In this study, the dependence of Er addition (0-0.49 wt %) on the microstructural evolution and related tensile strength at high temperature (HT) were investigated for the eutectic Al-Si piston alloys. The results showed there were intermetallic compounds of -Al3CuNi, -Al7Cu4Ni, Al4Cu2Mg8Si7, β-AlFeSi and Al3(Er, Cu, Fe) (Ni, Si) 2 identified at T5 states. Herein, the added Er element has led to the formation of the star-like and the irregular-shaped Al3(Er, Cu, Fe) (Ni, Si) 2 phase. The phase was stable which showed little change in both size and composition experienced solid solution at HT during the T6 treatment. For the HT strengths (350 oC), the T5 state alloys have higher UTSs than those at T6 state, both of which were reduced gradually with the increasing Er contents. The variation of HT strengths caused by the Er addition was explained by the microstructral evolution, namely Al3(Er, Cu, Fe) (Ni, Si)2 phase formation
Publisher
Kaunas University of Technology (KTU)
Subject
General Materials Science
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献