Abstract
ABSTRACT
Precipitated silica- and carbon black (CB)-filled styrene-butadiene rubber (SBR) compounds and vulcanizates containing naphthenic oil (NO), soybean oil (SO), and modified soybean oil (MSO) were studied. Gel fraction; crosslink density; bound rubber fraction; curing behavior; and thermal, mechanical, and dynamic properties were compared. Interaction between SO, MSO, and silane coupling agent was also studied. It was shown that the incorporation of SO and MSO had similar effects in both silica- and CB-filled SBR compounds and vulcanizates. SO and MSO were found to consume curatives leading to a lower crosslink density and improved thermal stability of compounds and vulcanizates. In comparison with NO, MSO was found to increase the elongation at break and tensile strength, and the values of tan δ at 10 °C and 60 °C predict an increase of the wet traction performance and the rolling resistance to decrease the modulus and abrasion resistance. After adjusting the recipe, the modulus and abrasion resistance of the silica- and CB-filled SBR/MSO vulcanizates were tremendously increased, and the silica-filled SBR/MSO vulcanizates exhibited a better wet traction performance, a lower rolling resistance, and a better abrasion resistance simultaneously than the silica-filled SBR/NO vulcanizate.
Subject
Materials Chemistry,Polymers and Plastics
Cited by
16 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献