Performance of high sensitive heterojunction CuS/porous silicon photodetector

Author:

Ahmed A. A., ,Ali G. G.,Daham N. A., ,

Abstract

In this work, copper sulfide (CuS) nanostructure was deposited on a porous silicon wafer for the visible light by spray pyrolysis method. Through this, a series of devices were suggested as a part of the deposit concentration of CuS on n-type porous silicon. Simultaneously, the physical features of the attained film were illustrated. FESEM exhibited that the average nanoparticle diameter increased with the concentration of CuS at orientation (100) and was found to be 47.84 nm, 56.36nm and 71.32nm, while the average diameter at (111) orientation was found to be 37.64 nm, 41.46nm, 55.22 nm of 0.1, 0.3 and 0.5M respectively. In addition to the atomic force microscope (AFM) showed the roughness and uniformity of the CuS/PSi fabricated decreased with increasing concentration of CuS, In detail, the attained photo-responsivity and specific detectivity were observed to be 210 mW/A, 340 mW/A and 3×1010 Jones, 4.2×1010 Jones at orientation (100 )using concentration of 0.1M and 0.5M respectively . On the other hand, the photo-responsivity and specific detectivity were observed to be 260 mW/A, 380 mW/A and 1.8 ×1010 Jones, 4.5×1010 Jones at orientation (111) using concentrations of 0.1M and 0.5M respectively. The presented work shows a substitutional system for an economical and environmentally friendly optoelectronic scheme. The photo-responsive considered to be in a positive linear relationship with the used concentration.

Publisher

Virtual Company of Physics

Subject

General Physics and Astronomy,General Chemistry,Electronic, Optical and Magnetic Materials

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3