Inhibiting stress corrosion cracking of a prefabricated surface‐defective magnesium alloy thanks to biological organic components

Author:

Chen Lianxi12,Li Xiaorong1,Gu Haicheng1,Zhang Xueying3,Niu Ben3,Zhang Zhiguo4,Wang Xiaojian4,Chen Dongchu12,Zhao Chunwang12

Affiliation:

1. School of Materials Science and Hydrogen Energy Foshan University Foshan China

2. Guangdong Key Laboratory for Hydrogen Energy Technologies Foshan China

3. Guangdong Provincial Key Laboratory of Advanced Welding Technology China‐Ukraine Institute of Welding Guangdong Academy of Sciences Guangzhou China

4. Institute of Advanced Wear & Corrosion Resistant and Functional Materials Jinan University Guangzhou China

Abstract

AbstractBiomedical magnesium (Mg) alloys remain a challenge for their mainstream application, because the combination of bio‐mechanical stress and corrosive physiological environment leading to stress corrosion cracking (SCC). It is crucial to avoid the sudden brittle fracture of Mg alloys in vivo for predicting their service duration. However, the key factors, such as surface or physiological environment features, determining the origination or propagation of SCC behavior are still unclear. In the present study, a prefabricated surface defects coating was prepared by the phytic acid (PA, C6H18O24P6) conversion treatment. Four mimicking physiological media were used, ranging from simple to equivalent (Dulbecco's Modified Eagle Medium and Protein [DMEM+Pro]). The results showed that the PA film with numerous micro‐cracks provided limited protective ability in synthetic biological media. A striking finding was determined that although initial high corrosion rate of samples in DMEM+Pro led to an increased SCC nucleation, significant ductile fracture with elongation to failure (14.86%) was observed. Combined with the fracture features, the adsorption or deposition of biological composition into the tunnel of SCC cracks significantly inhibited the hydrogen embrittlement (HE) behavior. These results indicate that preventing the propagation of SCC crack by biological composition, rather than nucleation, plays a key role in avoiding the sudden fracture of Mg alloys. It provides a novel perspective to determine the non‐brittle fracture of Mg alloys for biomedical applications.

Funder

Basic and Applied Basic Research Foundation of Guangdong Province

Science and Technology Planning Project of Guangdong Province

Publisher

Wiley

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3