Abstract
AbstractBackground and ObjectivesThe aim of implantoplasty (IP) is to remove titanium implant layers that have been contaminated and to smoothen the implant surfaces so they retain less plaque. However, existing IP methods are very invasive and reduce implant wall thickness.AimTo investigate the suitability of novel sonic tips in IP and to compare this novel protocol with conventional abrasive procedures.Materials and MethodsThirty dental implants (Ø 4.1 mm, 10 mm length) were distributed in three groups and investigated according to the protocol of Sivolella et al., with modifications to the instrument's feed rate, the applied contact force, and the speed of implant rotations per minute. The upper third of the implant was processed with a diamond‐coated bur (BUR) or novel non‐diamond‐coated sonic tips (AIRSCALER). After standardized IP, the surfaces were analyzed by tactile profilometry and scanning electron microscopy (SEM). Changes in implant weight, implant material loss, and implant fracture strength were assessed.ResultsThe mean roughness (Ra, Sa), implant material loss, and change in implant weight were significantly lower in the AIRSCALER group than in the BUR group, whereas the mean compression resistance values were significantly higher in the AIRSCALER group than in the BUR group.ConclusionsIP with uncoated sonic tips smoothes the surfaces and reduces structural loss of the implant in the area of microthreads. This new IP method could be of great clinical importance, especially for implants with microthreads and reduced diameter or wall thickness.