Experimental investigation and life prediction of hot corrosion pre-exposure on low-cycle fatigue of a directionally solidified nickel-base superalloy-Reference-Cited by-同舟云学术

Experimental investigation and life prediction of hot corrosion pre-exposure on low-cycle fatigue of a directionally solidified nickel-base superalloy

Published:2015-03-22 Issue:10 Volume:38 Page:1155-1166
ISSN:8756-758X
Container-title:Fatigue & Fracture of Engineering Materials & Structures
language:en
Short-container-title:Fatigue Fract Engng Mater Struct

Author:

Li S. L.¹,Yang X. G.¹²,Qi H. Y.¹²,Ma L. Q.¹³,Yang J. S.¹,Shi D. Q.¹

Affiliation:

1. School of Energy and Power Engineering; Beihang University; Beijing 100191 China

2. Collaborative Innovation Center of Advanced Aero-Engine; Beijing 100191 China

3. Shenyang Engine Design and Research Institute; Aviation Industry Corporation of China; Shenyang 110015 China

Publisher

Wiley

Subject

Mechanical Engineering,Mechanics of Materials,General Materials Science

Link

http://onlinelibrary.wiley.com/wol1/doi/10.1111/ffe.12295/fullpdf

Reference42 articles.

1. Investigation of the mechanisms of Type-II hot corrosion of superalloy CMSX-4;Lortrakul;Corros. Sci.,2014

2. Failure analysis of a gas turbine blade made of Inconel 738LC alloy;Mazur;Eng. Fail. Anal.,2005

3. Failure assessment of Nimonic 80A gas turbine blade;Kargarnejad;Eng. Fail. Anal.,2012

4. Analysis of superalloy turbine blade tip cracking during service;Xie;Eng. Fail. Anal.,2006

5. Corrosion failures in gas turbine hot components;Kosieniak;J. Fail. Anal. Prev.,2012

Cited by 14 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Fatigue behaviors of a nickel-based superalloy after hot-corrosion: Experiments and peridynamic simulations;International Journal of Fatigue;2024-03

2. Low-cycle fatigue behavior of DZ125 superalloy under prior exposure conditions;RARE METALS;2023

3. Damage evolution and life modeling of hot corrosion environment on creep‐fatigue of a directionally solidified nickel‐based superalloy;Fatigue & Fracture of Engineering Materials & Structures;2023-01-04

4. A modified constitutive model considering microstructure degradation of Ni-based superalloys and its application to microstructural damage calculation;Journal of Alloys and Compounds;2021-11

5. Effects of Hot Corrosion on Fatigue Performance of GH4169 Alloy;Journal of Materials Engineering and Performance;2021-02-09