Effect of Na2SiO3 concentration on corrosion resistance and wear resistance of MAO ceramic film on the Al‐Mg‐Sc alloy

Abstract

AbstractAlthough Al‐Mg‐Sc alloy was widely applied to aviation aerospace field, they were vulnerable to local corrosion and wear in the process of long‐term service in severe environmental conditions. In this paper, micro‐arc oxidation (MAO) ceramic films on Al‐Mg‐Sc alloy substrate were prepared in electrolyte solutions with different Na2SiO3 concentrations, and the corrosion resistance and wear resistance of the MAO samples were studied. The experimental results of potentiodynamic polarization (PDS) and long‐term immersion tests indicated that the MAO ceramic film prepared in 10 g/L Na2SiO3 electrolyte solution had the best corrosion resistance, as manifested by no obvious cracks, serious collapse and corrosion products on the sample surface and no deep cracks and corrosion paths in the cross‐sectional area. The increase of Na2SiO3 concentration in electrolyte solution also improved the wear resistance of MAO ceramic film, as manifested by low wear depth (10 μm)and width (1 mm) of the MAO ceramic film prepared in 10 g/L Na2SiO3 electrolyte solution against GCr15 steel ball. Studies in mechanisms suggested that as the Na2SiO3 concentration in the electrolyte increased, the MAO ceramic film became denser, which could prevent the penetration of corrosive medium, promote the generation of the anti‐wear layer with SiO2 as the main component to enhance the wear resistance. MAO ceramic film formed in Na2SiO3 electrolyte solution provided good protective performance for Al‐Mg‐Sc alloy in the corrosion and wear conditions, which had a broader application prospect.