Effect of alumina sol on the preparation of magnesia‐alumina spinel foam ceramics by foaming‐sol method

Author:

Sun Gege1,Li Guohua1ORCID,Jiao Changfa1,Tian Lin1ORCID,Deng Shudan1

Affiliation:

1. School of Materials and Metallurgy University of Science and Technology Liaoning Anshan China

Abstract

AbstractIn this work, magnesia‐alumina spinel foam ceramics were prepared by foaming‐sol method using magnesia alumina spinel as raw material, anionic surfactant potassium oleate (PO) as foaming agent, and alumina sol as curing agent. The curing mechanism and the effect of alumina sol content on the stability of foam slurry and the properties of foam ceramics were investigated. In the foam slurry, the alumina sol can react with PO, so magnesia‐alumina spinel can be fixed in the foam structure through the gel network to improve the stability of the foam slurry. The gelation process reduces the viscosity of the foam slurry. The pores of magnesia‐alumina spinel foam ceramics sintered at 1500°C are mostly closed pores and the average pore was 29.7–42.1 µm. With the increase of alumina sol content, the bulk density of magnesia‐alumina spinel foam ceramics increased from 1.3 to 1.9 g/cm3, the cold compressive strength from 8.8 to 22.7 MPa, and the thermal conductivity from .417 to .806 W·m−1·K−1(350°C).

Funder

National Key Research and Development Program of China

Publisher

Wiley

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3