Affiliation:
1. Institute of Nuclear Physics and Chemistry China Academy of Engineering Physics Mianyang China
Abstract
AbstractTwo high‐entropy carbides, including stoichiometric (Zr,Ti,Nb,Ta,Hf)C and nonstoichiometric (Zr,Ti,Nb,Ta,Hf)C0.8, were prepared from monocarbides and ZrH2. Their sinterability, microstructures, mechanical properties, thermophysical properties, and oxidation behaviors were systematically compared. With the introduction of carbon vacancy, the sintering temperature was lowered up to 300°C, Vickers hardness was almost unaffected, whereas the strength decreased significantly generally due to the decrease of covalent bonds. The thermal conductivity shows a 50% decrease for nonstoichiometry high‐entropy carbide, which is a major consequence of the lower electrical conductivity. The oxidation resistance in high temperature water vapor was not sensitive to carbon stoichiometry.
Funder
National Natural Science Foundation of China
Subject
Materials Chemistry,Ceramics and Composites
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献