The effect of hydrogen on the fracture toughness of friction‐stir welded API 5L X70 pipeline steels-Reference-Cited by-同舟云学术

The effect of hydrogen on the fracture toughness of friction‐stir welded API 5L X70 pipeline steels

Published:2022-08-10 Issue:10 Volume:45 Page:3009-3024
ISSN:8756-758X
Container-title:Fatigue & Fracture of Engineering Materials & Structures
language:en
Short-container-title:Fatigue Fract Eng Mat Struct

Author:

Giarola Joseane M.¹^ORCID,Avila Julian A.²³^ORCID,Cintho Osvaldo M.⁴,Pinto Haroldo C.¹,de Oliveira Marcelo F.¹,Bose Filho Waldek W.¹

Affiliation:

1. São Carlos School of Engineering (EESC) University of São Paulo (USP) São Carlos Brazil

2. Department of Strength of Materials and Structural Engineering, Barcelona School of Engineering (ETSEIB) Universitat Politècnica de Catalunya Barcelona Spain

3. Campus of São João da Boa Vista São Paulo State University (UNESP) São João da Boa Vista Brazil

4. State University of Ponta Grossa (UEPG) Ponta Grossa Brazil

Funder

Conselho Nacional de Desenvolvimento Científico e Tecnológico

Publisher

Wiley

Subject

Mechanical Engineering,Mechanics of Materials,General Materials Science

Link

https://onlinelibrary.wiley.com/doi/pdf/10.1111/ffe.13799

Reference98 articles.

1. Strength–hardness statistical correlation in API X65 steel

2. Improved resistance to hydrogen embrittlement of friction stir welded high carbon steel plates

3. Hydrogen diffusion and trapping in X70 pipeline steel

4. The mechanism of failure by hydrogen induced cracking in an acidic environment for API 5L X70 pipeline steel

5. Friction stir process now welds steel pipe;Defalco J;Weld J,2009

Cited by 9 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Molecular dynamics study on the effect of hydrogen on the plastic behavior of α-Fe crack tip;Materials Today Communications;2024-06

2. Embrittlement, degradation, and loss prevention of hydrogen pipelines;MRS Bulletin;2024-04-04

3. The effect of hydrogen and notch orientation in SENT specimens on the fracture toughness of an API 5L X70 pipeline steel;Engineering Fracture Mechanics;2024-04

4. Effect of microstructure on hydrogen embrittlement and hydrogen-induced cracking behaviour of a high-strength pipeline steel weldment;Corrosion Science;2024-02

5. Modeling of necking area reduction of carbon steel in hydrogen environment using machine learning approach;Engineering Failure Analysis;2024-02