Abstract
Studies of experimental adhesion modifiers based on a mixture of fatty acids from the production of light vegetable oils. The properties of rubber compounds and their vulcanizates obtained using experimental adhesion promoters KK with cobalt content from 7.5 to 16.5% are investigated. The plastic-elastic and vulcanization properties of the properties of breaker rubber compounds based on polyisoprene, the physical and mechanical properties of breaker rubbers and the bond strength in the “rubber-brass-plated steel cord system” were studied. When testing belt rubbers containing experienced adhesion promoters or an imported analog of Manobond 680C, the following features were revealed. The plasticity of the prototypes was in the range of 0.2-0.4. This indicates satisfactory processing properties. The Mooney viscosity of the prototypes was lower than that of the production sample. The use of experienced adhesion promoters instead of the analogue (Manobond 680C) increases the resistance to scorching. On the basis of the analysis of elastic-strength properties, it was found that in terms of the conditional tensile strength, the prototypes were inferior to the serial ones. However, rubbers containing the KK-12, KK-13.5, KK-15 promoters met the control standards. The tensile elongation at break of the experimental rubbers is higher than that of the serial sample. This may indicate the formation of a more uniform cure network in the presence of the test products. When testing rubber-metal-hard composites, it was noted that, under normal conditions, the experienced adhesion promoters have advantages over Manobond 680C. However, at elevated temperatures, under conditions of salt and steam-air aging, they are slightly inferior to Manobond 680C. It has been established that the experimental adhesion promoters provide the required set of technical properties of belt rubbers with a CO2 + content of 12–16.5% wt. Thus, it is possible to recommend the adhesion promoters KK 12, KK-13.5, KK 15 for practical use in the composition of belt rubber compounds. This will allow replacing a foreign-made product and reducing the cost of production.
Publisher
FSBEI HE Voronezh State University of Engineering Technologies
Subject
General Agricultural and Biological Sciences
Reference15 articles.
1. Kablov V.F., Lapin S.V., Puchkov A.F., Shmurak I.L. Some promoters of adhesion of steel cord to rubber. Rubber and rubber. 2014. no. 5. pp. 42–43. (in Russian).
2. Shmurak I.L. Adhesion joint metal cord / rubber. Formation and destruction. Rubber and rubber. 2013. no. 2. pp. 56-60. (in Russian).
3. Bobrov A.P., Drobot D.V., Lyakin Yu.I., Potapov E.E. et al. Cobalt - nanomodified shungite as a promoter of rubber adhesion to steel cord. Rubber and rubber. 2016. no. 3. pp. 24–28. (in Russian).
4. Buytaert G., Luo Y. Study of Cu-Zn-Co ternary alloy-coated steel cord in cobalt-free skim compound. Journal of Adhesion Science and Technology. 2014. vol. 28 (6).
5. Kasperovich A.V., Krotova O.A., Potapov E.E., Reznichenko S.V. et al. The effect of modified silica on the adhesion of rubber to steel cord. Bulletin of the Technological University. 2014. vol. 17 (14). pp. 235–237. (in Russian).