AN ASSESSMENT OF VARIOUS NANOADDITIVES AND TRIBO-CORROSION WITH WASTE COOKING BIODIESEL FUELED IN A DIESEL ENGINE

Abstract

The waste cooking biodiesel's steady-state coefficient of friction rate of fuel blends are B90 (18.2%), B60 (7.2%), B20 (16.72%), B10 (30.8%), and diesel (38.77%) higher compared with B40 fuel blend and wear scar diameter of the fuel blends from B40 to B100 had a minimal range of 0.5mm. The flash temperature parameter results higher from B40 to B100 fuel blends, and the corrosion rate was minimal for B40 and B50 fuel blends. Afterward, the fuel blend B40 (40% WCO+60% Diesel fuel) was chosen as fuel, along with Cerium (25ppm), Zinc (25ppm), and Titanium nanoparticles (25ppm) were selected as fuel additives. The B40+D60+Titanium (25ppm) blend resulted in improved BTE and 3.83% lowered BSEC comparison with diesel fuel. Then the fuel blend, B40+D80+Titanium (25ppm), resulted in 2.08% reduced HC, 36.36% CO, and 16.25% smoke emissions, along with marginally 8.5% higher NOx emissions comparison with diesel fuel. Also, the fuel blend, B40+D80+Titanium (25ppm) combustions characteristics are the equivalent trend of cylinder pressure (58.82 bar) and HRR (66.65 J/deg CA) related to diesel fuel at peak load.