Abstract
The glass system (50–x)B2O3–30Bi2O3–20TeO2–xEu2O3 (x = 0, 0.1, 0.5, 1.0, 1.5, and 2.0 mol%) having been prepared using the conventional melt quenching method, is investigated in terms of physical, optical, and luminescence properties. The density of these glasses is measured and the corresponding molar volume is also calculated. The (αhν)1/n versus hν graph was plotted and it is well fitted to both direct (n = 1/2) and indirect (n = 2) band gaps. The direct and indirect band gap values range from 2.57 to 2.94 eV and 1.74 to 2.58 eV, respectively. The Urbach energy of the glass system was calculated to have values ranging from 0.29 to 0.62 eV. Yellow, orange, and red emissions have been observed through photoluminescence (PL) spectroscopy excited at 464 nm and the obtained multicolor emissions have been demonstrated according to the Commission International de l’Eclairage de France 1931 standards. The results of PL studies indicated the possibility towards the development of multicolor phosphor applications.
Publisher
Canadian Science Publishing
Subject
General Physics and Astronomy
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献