Comparative Study of Joint Performance According to Joining Methods Between Al7075-T6 and SPFC590DP for Lightweight Car Body

Author:

Cho Keong HwanORCID,Joo Jin HyeokORCID,Lee Jung Heum,Oh Je Hoon,Kam Dong HyuckORCID

Abstract

The necessity of dissimilar joining between aluminum alloy and steel is increasing in order to meet the demand for weight reduction in automobiles. However, dissimilar joining between 7000 series aluminum alloy and steel is challenging with mechanical joining methods such as self-piercing rivet(SPR) and flow drill screw(FDS) without hole processing. In this study, mechanical performances of dissimilar joints between 3 mm thick Al7075-T6 and 1 mm thick SPFC590DP were evaluated for use in lightweight B-pillar assembly. Self-Piercing Rivet(SPR) and Flow Drill Screw(FDS) with one-hole processing, bolt/nut and blind rivet with two-hole processing and adhesive bonding were compared with respect to joint performance. In SPR joining, rivet did not penetrate and rivet buckling occurred in the rivet due to the thickness and high strength of the Al7075-T6. By processing pre-hole on Al7075-T6 and applying an additional Al5052-H32 sheet to induce mechanical interlock in SPR joint, it became possible to join Al7075-T6 to SPFC590DP with an SPR. The tensile shear load of the SPR joint was 9.8 kN. In FDS joining, it is also necessary to process pre-hole on Al7075-T6 since the fastener could not penetrate the Al7075-T6. The tensile shear load of the FDS joining was 8.1 kN. In bolt/nut and blind rivet joining, the tensile shear load were measured respectively 11.1 kN and 5.2 kN. In adhesive bonding with 1K glue, the tensile shear load was measured 18.5 kN when the interfacial surface was roughened with a sand paper.

Funder

Ministry of Trade, Industry and Energy

Publisher

The Korean Welding and Joining Society

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3