Ultrasmooth Ti/Al multilayer with a Ti seed layer for EUV applications

Abstract

Al-base multilayers have attracted much interest in the extreme ultraviolet (EUV) optics field, but high roughness of this multilayer due to the Al film is still a big concern. Here, a strategy of the seed layer was proposed to reduce the surface roughness and intermixing layer thickness of the Al-base multilayer. Ti film is not only a seed layer, but also an absorption layer in this novel multilayer. An optimized Ti/Al multilayer film structure was designed to work at 21.1 nm, while investigating the use of Ti as a seed layer to reduce the roughness and enhance the peak reflectivity. The experimental results showed that the Ti seed layer effectively reduced the surface roughness and intermixing layer thickness and improved the reflectance. At 21.1 nm, the peak reflectance reached 39.6%, with a bandwidth of only 1.0 nm and an RMS roughness of 0.17 nm. Ti/Al multilayer also exhibits good stability. This multilayer has potential application in high-precision optics, such as corona detection, which requires extreme low light scattering of multilayer mirror.