Abstract
InGaAs/AlGaAs multiple quantum well lasers grown on silicon (001) by molecular beam epitaxy have been demonstrated. By inserting InAlAs trapping layers into AlGaAs cladding layers, misfit dislocations easily located in the active region can be effectively transferred out of the active region. For comparison, the same laser structure without the InAlAs trapping layers was also grown. All these as-grown materials were fabricated into Fabry-Perot lasers with the same cavity size of 20 × 1000 µm2. The laser with trapping layers achieved a 2.7-fold reduction in threshold current density under pulsed operation (5 µs-pulsed width, 1%-duty cycle) compared to the counterpart, and further realized a room-temperature continuous-wave lasing with a threshold current of 537 mA which corresponds to a threshold current density of 2.7 kA/cm2. When the injection current reached 1000 mA, the single-facet maximum output power and slope efficiency were 45.3 mW and 0.143 W/A, respectively. This work demonstrates significantly improved performances of InGaAs/AlGaAs quantum well lasers monolithically grown on silicon, providing a feasible solution to optimize the InGaAs quantum well structure.
Funder
National Key Research and Development Program of China
Beijing Municipal Science and Technology Commission
National Natural Science Foundation of China
111 Project
the Funds for Creative Research Groups of China
State Key Laboratory of Information Photonics and Optical Communications
Fundamental Research Funds for the Central Universities
Subject
Atomic and Molecular Physics, and Optics
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献