Ghelloudj Elhadj,Hannachi Mohamed Tahar,Djebaili Hamid
Abstract
In the present research, AISI 4140 steel was nitrided in salt bath to study and analyze the behaviour of the surface roughness. The structural surface characterization behaviour of the nitrided steel was compared to the behaviour of the same steel which was untreated. The nitriding process was implemented in the salt bath component at ten different times (from 1 h to 10 h) when the temperature was constant at (580ºC). The influence of nitriding treatment on structural properties of the material was studied by scanning electron microscopy (SEM), microhardness tester and surface profilometer. It was found that salt bath nitriding was effective in improving the surface properties behaviour of this steel. Experimental results showed that the nitrides ε-Fe2-3(N,C) and γ’-Fe4(N,C) present in the compound layer increase the microhardness (406–502 HV0.3), the initial surface roughness values of nitrided samples were higher than those of unnitrided specimens, it also observed that the increasing the nitriding time increases the surface roughness parameters (Ra, Rq and Rz).
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献