Effect of Incorporating Chitosan to Resin Modified Glass Ionomer Cement on Shear Bond Strength to Dentin (An In vitro Comparative Study)

Author:

Khudhair Aya Tahseen1,Khalaf Muna Saleem2

Affiliation:

1. Pedodontic Dentistry Department, College of Dentistry, University of Baghdad, Baghdad, Iraq

2. Pedodontic & Preventive Dentistry Department, College of Dentistry, University of Baghdad, Baghdad, Iraq

Abstract

Abstract Aim: Resin-modified glass ionomer cement tends to shrink due to polymerization of the resin component. Additionally, they are more prone to syneresis and imbibition during the setting process. This in vitro study evaluates the impact of chitosan, a biopolymer that is, both biomaterial and biocompatible, on the strength of dentin bonding and compares it with ACTIVA Bio-ACTIVE Restorative. The present study was aimed to assess the impact of including chitosan into Fuji II on the shear bond strength between. the restoration material and tooth dentin, in contrast to Bioactiva in permanent teeth. Materials and Methods: A total of 30 premolar teeth were recently extracted. The study involved three distinct sample groups. Group 1 (10 teeth) is the negative control (Fuji II), Group 2 (10 teeth) is the positive control (ACTIVA Bio-ACTIVE Restorative), and Group 3 (10 teeth) is treated with a mixture of Chitosan and Fuji II (CH-Fuji II). Each tooth’s buccal and palatal cusps were eliminated to achieve a horizontal surface. Using a periodontal probe, 1.5 mm from the mesial pit to the mesial marginal ridge were removed. Restoration was implemented in all groups following manufacturer directions. Thermocycling the teeth by immersing them in a water bath with temperatures ranging from 5°C to 55°C (± 1–2°C) for 30 s (500 cycles). Each sample was attached to the universal testing machine’s jig at a cross-head speed of 1 mm/min. Shear force was used until breakage, and the bond’s adhesive strength was then calculated. Statistical analysis using ANOVA with Dunnett’s T3 post hoc test. Results were significant at P < 0.05. Results: Statistically significant difference was present between Chitosan and Fuji II and between Chitosan and Activa by reducing the shear bond strength. Conclusions: Addition of chitosan to Fuji II had a negative effect on the shear bond with a significant difference while Activa and Fuji II exhibited favorable shear bond strength.

Publisher

Medknow

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3