The Effect of Different Ageing Protocols on the Shear Bond Strength of the Ceromer Indirect Composite on Two Different Substructure Materials

Author:

Kuscu HY Yay1

Affiliation:

1. Department of Prosthodontics, Faculty of Dentistry, Mehmet Akif Ersoy University, Burdur, Turkey

Abstract

Backround: The evolution of restorative materials in prosthodontics has led to the emergence of indirect composite resins, including ceromers, as alternatives to traditional metal-ceramic restorations. However, research gaps exist regarding the impact of ageing protocols on the bond strength of ceromer composites to different metal substructures, necessitating further investigation in this area. Aim: This study aimed to determine the effect of five different ageing protocols on the shear bond strength (SBS) of ceromer indirect composites on two different substructures. Methods: In this in vitro study, 120 metallic discs (10 × 2 mm) were cast from cobalt-chromium (Co-Cr) alloy (n = 60) and spark erosion treated from grade V titanium (n = 60). Each sample was sandblasted. The M.L. primer (Shofu, Germany) and layers of opaque were applied to the surface following the manufacturer’s instructions. A special jig (6 × 2 mm) was placed on each disc. The ceromer was condensed in it and light-cured separately for 90 s. Following polishing, specimens were separated into five ageing groups: distilled water (as a control), thermal cycling, tea, coffee, and gastric acid immersion. All samples were placed in 37°C incubation for 28 days for distilled water, coffee, and tea, and 7 days for gastric acid immersion and thermal cycling for 5000 cycles (5-55°C). A universal test machine was used to measure the SBS. The samples were evaluated for failure modes using stereomicroscopy. Data were analyzed using one-way analysis of variance (ANOVA) (P < 0.05). Results: According to one-way ANOVA, the mean SBS (MPa) between the two groups was compared in each ageing protocol, and there were no significant differences between the Co-Cr-C and Ti-C groups (P > 0.05). The most frequent mode of failure in all groups was mixed. Conclusions: Applying the ageing protocols, the type of substructure material had no significant effect on the SBS of the ceromer indirect composite except for tea immersion.

Publisher

Medknow

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3