Influence of exposure to aggressive environment on fatigue behavior of a shot peened high strength aluminum alloy

Published:2013-07 Issue: Volume:574 Page:243-252
ISSN:0921-5093
Container-title:Materials Science and Engineering: A
language:en
Short-container-title:Materials Science and Engineering: A

Author:

Sheng-Li Lv,Cui You,Gao Xiaosheng,Srivatsan T.S.

Funder

National Key Technology Research and Development (R&D)

Publisher

Elsevier BV

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science

Reference17 articles.

1. Effects of pitting corrosion on the fatigue behavior of aluminum alloy 7075-T6: modeling and experimental studies

2. Characterization of pitting damage and prediction of remaining fatigue life

3. M. Liao, G. Renauld, N.C. Bellinger, in: Proceedings of the Eighth Joint NASA/FAA/DoD Conference on Aging Aircraft, Palm Springs, CA, USA, 2005.

4. M. Liao, G. Renauld, D. Backman, in: Proceedings of Second International Conference on Environment-induced cracking of metals, Banff, Canada, 2004.

5. NATO Applied Vehicle Technology Panel on Fatigue in the Presence of Corrosion;Worsfold,1999

Cited by 9 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Review of Residual Stress Impingement Methods to Mitigate Environmental Fracture Susceptibility;Corrosion and Materials Degradation;2021-10-20

2. The fatigue crack behavior of 7N01-T6 aluminum alloy in different particle environments;Archives of Civil and Mechanical Engineering;2020-10-17

3. Acceleration effect of a graphite dust environment on the fatigue crack propagation rates of Al alloy;International Journal of Fatigue;2019-09

4. Shot Peening Numerical Simulation of Aircraft Aluminum Alloy Structure;IOP Conference Series: Materials Science and Engineering;2018-03

5. Surface integrity evolution and fatigue evaluation after milling mode, shot-peening and polishing mode for TB6 titanium alloy;Applied Surface Science;2016-11